Zairyo-to-Kankyo Vol. 64 (2015), No. 2

  • Prosperity and Decline of Corrosion Studies at University

    pp. 25-25

    Bookmark

    You can use this feature after you logged into the site.
    Please click the button below.

    Log in / Sign Up

    DOI:10.3323/jcorr.64.25

  • Evaluation and Monitoring Methods for Atmospheric Corrosion

    pp. 26-33

    Bookmark

    You can use this feature after you logged into the site.
    Please click the button below.

    Log in / Sign Up

    DOI:10.3323/jcorr.64.26

    Methods and techniques to monitor and evaluate corrosivities in atmospheric environments are introduced including an ACM (Atmospheric Corrosion Monitor) type corrosion sensor, which was developed by authors. For the ACM sensor, the occurrence and duration of rain, dew and dry periods, Train, Tdew and Tdry, respectively, could be distinguished and determined by analyzing the magnitude and time variation of sensor output, I. And by referencing to the empirical I-RH calibrating curve, the amount of deposited sea salt, Ws, could also be estimated. Effects of those environmental factors - RH, Ws, Train, Tdew and Tdry, and so on - on the corrosion behaviors of steels - carbon steel, galvanized steel and stainless steels - are discussed. Moreover, equations to estimate corrosion rate of carbon steel were suggested with those factors and electricity of ACM sensor output.
  • Inhibition of Cobalt Corrosion by Silane Coupling Treatment

    pp. 42-50

    Bookmark

    You can use this feature after you logged into the site.
    Please click the button below.

    Log in / Sign Up

    DOI:10.3323/jcorr.64.42

    Improvement of corrosion resistance of a thin cobalt film by the surface treatment using 1, 2-Bis(triethoxysilyl) ethane (BTSE) was evaluated. A BTSE layer was formed on cobalt oxide by immersing the cobalt film in a BTSE solution including water and hydrogen peroxide which improved corrosion resistance of the film significantly. When hydrogen peroxide was absent in the BTSE solution, the BTSE layer was not formed. The corrosion resistance was improved with increasing the pH of BTSE solution containing hydrogen peroxide. These behaviors could be explained by the hard and soft acid-base (HSAB) principle.
  • Propagation Analysis of Crevice Corrosion on SUS304 Stainless Steel Under Potentiostatic Condition in Artificial Sea Water

    pp. 51-59

    Bookmark

    You can use this feature after you logged into the site.
    Please click the button below.

    Log in / Sign Up

    DOI:10.3323/jcorr.64.51

    The propagation behavior of crevice corrosion on SUS304 was investigated by the new crevice corrosion test apparatus. The corrosion area and corrosion current in glass/metal crevice can be measured at the same time by this apparatus. The specimen was polished just before the crevice corrosion test under the constant potential condition, E=299 mV, 399 mV and 499 mV (SHE), in artificial seawater at room temperature. Some important results were obtained. The crevice corrosion initiation time tVI determined by the visual observation was coincident with tINCU determined by the current density change. The crevice corrosion area, ACREV, increased exponentially with time from the crevice corrosion initiation time. However, the increasing rate of the crevice corrosion volume, VCREV, changed at the time, tR, which crevice corrosion reached at the edge of crevice. We divided the corrosion process into two stages, Region I and Region II. Region I and Region II are defined as the time region before and after tR respectively. The increasing rate of VCREV in Region II was larger than that in Region I. However, the increasing rate of ACREV in Region I was slightly larger than that in Region II.

Article Access Ranking

16 Jan. (Last 30 Days)

  1. A Review of the Chemistry, Structure and Formation Conditions of Silico-Ferrite of Calcium and Aluminum (‘SFCA’) Phases ISIJ International Vol.58(2018), No.12
  2. Improving Blast Furnace Raceway Blockage Detection. Part 1: Classification of Blockage Events and Processing Framework ISIJ International Advance Publication
  3. Phase Transformation Behavior of Oxide Scale on Plain Carbon Steel Containing 0.4 wt.% Cr during Continuous Cooling ISIJ International Vol.58(2018), No.12
  4. Hydrogen Embrittlement Susceptibility Evaluation of Tempered Martensitic Steels Showing Different Fracture Surface Morphologies Tetsu-to-Hagané Vol.105(2019), No.1
  5. Improvement of Sinter Productivity by Control of Magnetite Ore Segregation in Sintering Bed ISIJ International Vol.58(2018), No.12
  6. Gasification and Migration of Phosphorus from High-phosphorus Iron Ore during Carbothermal Reduction ISIJ International Vol.58(2018), No.12
  7. Effect of TiO2 and MnO on Viscosity of Blast Furnace Slag and Thermodynamic Analysis ISIJ International Vol.58(2018), No.12
  8. Effect of Coke Size on Reducing Agent Ratio (RAR) in Blast Furnace ISIJ International Vol.58(2018), No.12
  9. High Temperature Thermal Diffusivity Measurement for FeO Scale by Electrical-Optical Hybrid Pulse-Heating Method ISIJ International Vol.58(2018), No.12
  10. Improving Blast Furnace Raceway Blockage Detection. Part 3: Visual Detection Based on Tuyere Camera Images ISIJ International Advance Publication

Search Phrase Ranking

16 Jan. (Last 30 Days)

  1. blast furnace
  2. blast furnace permeability
  3. blast furnace productivity
  4. 鉄と鋼
  5. continous annealing
  6. laser welder
  7. titanium
  8. a
  9. activity feo
  10. argon steel