材料と環境 Vol. 73 (2024), No. 4
Backnumber
-
Vol. 73 (2024)
-
Vol. 72 (2023)
-
Vol. 71 (2022)
-
Vol. 70 (2021)
-
Vol. 69 (2020)
-
Vol. 68 (2019)
-
Vol. 67 (2018)
-
Vol. 66 (2017)
-
Vol. 65 (2016)
-
Vol. 64 (2015)
-
Vol. 63 (2014)
-
Vol. 62 (2013)
-
Vol. 61 (2012)
-
Vol. 60 (2011)
-
Vol. 59 (2010)
-
Vol. 58 (2009)
-
Vol. 57 (2008)
-
Vol. 56 (2007)
-
Vol. 55 (2006)
-
Vol. 54 (2005)
-
Vol. 53 (2004)
-
Vol. 52 (2003)
-
Vol. 51 (2002)
-
Vol. 50 (2001)
-
Vol. 49 (2000)
-
Vol. 48 (1999)
-
Vol. 47 (1998)
-
Vol. 46 (1997)
-
Vol. 45 (1996)
-
Vol. 44 (1995)
-
Vol. 43 (1994)
-
Vol. 42 (1993)
-
Vol. 41 (1992)
-
Vol. 40 (1991)
キーワードランキング
08 Sep. (Last 30 Days)
材料と環境 Vol. 73 (2024), No. 4
大気腐食の評価とモニタリング技術
篠原 正
pp. 85-96
DOI:
10.3323/jcorr.73.85抄録
Conventional electrochemical methods were considered difficult to apply to atmospheric corrosion with hardly to provide an electric current path. Recently, many sensors and measurement methods have been proposed to overcome that problem in corrosion monitoring under atmospheric environmental conditions. In this review, methods and techniques to monitor and evaluate atmospheric corrosion are introduced including an ACM (Atmospheric Corrosion Monitor) type corrosion sensor, which was developed by the authors. For the ACM sensor, it is shown that by analyzing the magnitude and time variation of the sensor output (I), it is possible to detect the periods of dew, drying, and rainfall and to measure their durations (Train, Tdew, Tdry). And it is also shown that by referencing to the empirical I-RH calibrating curve, it is possible to estimate the amount of sea salt deposition (Ws). Effects of those environmental factors -RH, Ws, Train, Tdew and Tdry, and so on – on the corrosion behaviors of steels - carbon steel, galvanized steel and stainless steels – are discussed. Moreover, the equations to estimate corrosion rate of carbon steel are suggested with those factors and electricity of ACM sensor output.
他の人はこちらも検索
材料と環境 Vol.73(2024), No.4
積雪環境下における鋼材の埋雪深さが鋼中水素量に与える影響
衣笠 潤一郎, 坂入 正敏
pp. 97-101
DOI:
10.3323/jcorr.73.97抄録
The amount of hydrogen in steel that affects hydrogen embrittlement is considered to be changed with the amount of corrosion of the steel. The authors have found a relationship between the depth of snow and the amount of corrosion. In this study, the hydrogen content was examined and no correlation was found with the amount of corrosion. Under thin solution layer formed by melting snow, the main cathodic reaction is reduction of dissolved oxygen and hydrogen generation reaction is slight. The large amount of surrounding water also suppresses the acidification of the thin solution layer on the specimen, suggesting that the reaction from Had to Hab by H+ formation and electron transfer is small.
他の人はこちらも検索
材料と環境 Vol.73(2024), No.4
ガンマ線照射下にある高温水中でのステンレス鋼隙間内腐食挙動における溶存酸素の影響
佐藤 智徳, 端 邦樹, 加藤 千明, 五十嵐 誉廣
pp. 102-109
DOI:
10.3323/jcorr.73.102抄録
In order to evaluate the effects of dissolved oxygen concentration on the radiolytic water quality within the cracks of stress corrosion cracking (SCC) under irradiation and the spatial distribution of water quality along the depth axis during irradiation, we conducted immersion tests of stainless steel with a crevice gap and computational simulations of water radiolysis. It has been confirmed that Fe2O3 is formed throughout the entire crevice region, irrespective of the dissolved oxygen concentration. Furthermore, it has been estimated that oxidant species generated by radiolysis within the crack are consumed by the growth of oxides under irradiation, and that the reduction in pH at the crack tip occurs by hydrolysis of dissolved metallic elements and enrichment of anions.
論文アクセスランキング
08 Sep. (Last 30 Days)
-
Non-Isothermal Reduction Kinetics Model of Self-Reducing Iron Ore Pellets
ISIJ International Vol.64(2024), No.10
-
Effect of Wettability on Droplet Agglomeration in Two Immiscible Liquids
ISIJ International Vol.64(2024), No.8
-
Etching Behavior and Dielectric Film Formation on Aluminum Foil Stocks for Electrolytic Capacitors: A Review
MATERIALS TRANSACTIONS Vol.65(2024), No.8
-
Effect of P Addition on the Corrosion Resistance of Steels Before and After Rust Formation
ISIJ International 早期公開
-
中間熱処理を施した7%Ni鋼の極低温靭性に及ぼすMnの影響
鉄と鋼 Vol.110(2024), No.11
-
-
アロイ800Hの凝固特性とTiC生成挙動
鉄と鋼 早期公開
-
Coating Weight Reduction Technology in Gas Wiping of Hot-Dip Galvanizing on Steel Strip
ISIJ International 早期公開
-
Thermodynamic Calculation of Solute Carbon and Nitrogen in Nb and Ti Added Extra-low Carbon Steels
ISIJ International Vol.34(1994), No.1
-
Effect of Exit Wear Length on the Behavior of Coherent Jet
ISIJ International 早期公開
この機能はログイン後に利用できます。
下のボタンをクリックしてください。