材料と環境 Vol. 58 (2009), No. 7
Backnumber
-
Vol. 74 (2025)
-
Vol. 73 (2024)
-
Vol. 72 (2023)
-
Vol. 71 (2022)
-
Vol. 70 (2021)
-
Vol. 69 (2020)
-
Vol. 68 (2019)
-
Vol. 67 (2018)
-
Vol. 66 (2017)
-
Vol. 65 (2016)
-
Vol. 64 (2015)
-
Vol. 63 (2014)
-
Vol. 62 (2013)
-
Vol. 61 (2012)
-
Vol. 60 (2011)
-
Vol. 59 (2010)
-
Vol. 58 (2009)
-
Vol. 57 (2008)
-
Vol. 56 (2007)
-
Vol. 55 (2006)
-
Vol. 54 (2005)
-
Vol. 53 (2004)
-
Vol. 52 (2003)
-
Vol. 51 (2002)
-
Vol. 50 (2001)
-
Vol. 49 (2000)
-
Vol. 48 (1999)
-
Vol. 47 (1998)
-
Vol. 46 (1997)
-
Vol. 45 (1996)
-
Vol. 44 (1995)
-
Vol. 43 (1994)
-
Vol. 42 (1993)
-
Vol. 41 (1992)
-
Vol. 40 (1991)
材料と環境 Vol. 58 (2009), No. 7
グローバル二酸化炭素リサイクル
橋本 功二, 熊谷 直和, 加藤 善大, 泉屋 宏一
pp. 250-259
DOI:
10.3323/jcorr.58.250抄録
Extrapolation of world energy consumption between 1990 and 2006 to the future reveals the complete exhaustion of petroleum, natural gas, coal and uranium reserves on the Earth in 2037, 2042, 2055 and 2057, respectively. We are proposing global carbon dioxide recycling to use renewable energy by which all people in the whole world can survive. The electricity will be generated by solar cell in the deserts and used for production of hydrogen by seawater electrolysis at the nearby desert coasts. Hydrogen, for which no infrastructures of transportation and combustion exist, will be converted to methane at the desert coasts by the reaction with carbon dioxide captured by energy consumers. Among systems in global carbon dioxide recycling, seawater electrolysis and carbon dioxide methanation have not been performed industrially. We created energy-saving cathodes for hydrogen production and anodes for oxygen evolution without chlorine formation in seawater electrolysis, and ideal catalysts for methane formation by the reaction of carbon dioxide with hydrogen. The key factors for realization of global carbon dioxide recycling are the activity enhancement and corrosion prevention of those key materials.
乾湿繰り返し腐食環境下の鋼材に蓄積した水素の電気化学的測定による定量
小松 篤史, 西方 篤, 水流 徹
pp. 269-273
DOI:
10.3323/jcorr.58.269抄録
Hydrogen accumulated in eutectoid steels with different heat treatments was measured using electrochemical method. This method pulled out about 30% lesser amount of hydrogen than that determined by thermal desorption method. Hydrogen content in steels accumulated during single corrosion cycle was about 0.01 to 0.1 ppm and they depended on microstructure of steels. Hydrogen content in different microstructure of steels decreased in the order of: Martensite > pearlite > spheroidized cementite-ferrite. The amount of hydrogen accumulated during several continuous corrosion cycles was larger than that observed in single cycle, and the difference of hydrogen content between microstructures became also lager.
重炭酸塩溶液中における炭素鋼上の腐食皮膜形成
柴田 俊夫, 清水 義明
pp. 274-279
DOI:
10.3323/jcorr.58.274抄録
In order to understand the detailed corrosion process of carbon steel depending on pH in the neutral solution, corrosion film formation reaction on the steel surface in 0.01M NaHCO3 solution has been analyzed as a function of pH, the value of which was adjusted by bubbling a mixture of air and CO2 gas at an atmospheric pressure. It was found that precipitation ratio defined as the amount of precipitated film to the total corrosion loss increases with increase of pH, resulting in decrease of the total corrosion loss with increasing pH in the range between pH=3.5 and 10. Small addition of alloying elements such as Cu and Ni was also found to change the precipitation ratio. The film formation reaction is rationally explained by assuming that precipitation is decided by the solubility product of Fe(OH)2, Fe(OH)3 or FeCO3. The rate of corrosion was found to obey the parabolic low, suggesting that the diffusion of oxygen dissolved in the solution through the film controls the whole process.
論文アクセスランキング
26 Apr. (Last 30 Days)
-
Wettability of CaS Against Molten Iron at 1873 K
ISIJ International Vol.65(2025), No.2
-
Perspectives on the Promising Pathways to Zero Carbon Emissions in the Steel Industry toward 2050
ISIJ International Vol.65(2025), No.2
-
Thermodynamic evaluation of interaction parameters of solutes in molten iron
ISIJ International 早期公開
-
-
Prediction Studies of Strip Centering with Flotation Dryer
ISIJ International 早期公開
-
Ammonia as a Green Energy Carrier to Lower Blast Furnace CO2 Emissions
ISIJ International 早期公開
-
高感度電磁超音波による縦波横波ハイブリッド式連続鋳造クレーターエンド検知
鉄と鋼 Vol.111(2025), No.5
-
-
-
Preface
ISIJ International Vol.36(1996), No.Suppl
この機能はログイン後に利用できます。
下のボタンをクリックしてください。