材料と環境 Vol. 61 (2012), No. 8
Backnumber
-
Vol. 74 (2025)
-
Vol. 73 (2024)
-
Vol. 72 (2023)
-
Vol. 71 (2022)
-
Vol. 70 (2021)
-
Vol. 69 (2020)
-
Vol. 68 (2019)
-
Vol. 67 (2018)
-
Vol. 66 (2017)
-
Vol. 65 (2016)
-
Vol. 64 (2015)
-
Vol. 63 (2014)
-
Vol. 62 (2013)
-
Vol. 61 (2012)
-
Vol. 60 (2011)
-
Vol. 59 (2010)
-
Vol. 58 (2009)
-
Vol. 57 (2008)
-
Vol. 56 (2007)
-
Vol. 55 (2006)
-
Vol. 54 (2005)
-
Vol. 53 (2004)
-
Vol. 52 (2003)
-
Vol. 51 (2002)
-
Vol. 50 (2001)
-
Vol. 49 (2000)
-
Vol. 48 (1999)
-
Vol. 47 (1998)
-
Vol. 46 (1997)
-
Vol. 45 (1996)
-
Vol. 44 (1995)
-
Vol. 43 (1994)
-
Vol. 42 (1993)
-
Vol. 41 (1992)
-
Vol. 40 (1991)
材料と環境 Vol. 61 (2012), No. 8
水素を経て使える燃料の形での再生可能エネルギーの利用
橋本 功二, 熊谷 直和, 泉屋 宏一, 高野 裕之, 加藤 善大
pp. 305-313
DOI:
10.3323/jcorr.61.305抄録
Extrapolation of world energy consumption from 1990 to 2008 will result in the complete exhaustion of world reserves of oil, natural gas, uranium and coal until 2040, 2046, 2048 and 2054, respectively. For the survival of all people in the whole world, intermittent and fluctuating electricity generated from renewable energy should be supplied in the form of usable fuel to all people in the whole world. We are proposing global carbon dioxide recycling for the use of renewable energy in the form of methane via electrolytic hydrogen generation using carbon dioxide as the feedstock. We created energy-saving cathodes for hydrogen production, anodes for oxygen evolution without chlorine formation in seawater electrolysis and catalysts for methanation of carbon dioxide and built the pilot plants of industrial scale. Recent advance in materials is described. The industrial application is in progress.
加圧水型軽水炉2次系環境における銅系材料の腐食挙動
藤原 和俊, 堂前 雅史
pp. 327-334
DOI:
10.3323/jcorr.61.327抄録
In secondary systems of several pressurized water reactor (PWR) plants, operation conditions under a high pH in the presence of ammonia or ethanolamine (ETA) have been used, and the suppression of corrosion has been reported.
In PWR secondary systems, Cu alloys have been used for some of the structural components. Accordingly, it is necessary to investigate the corrosion behavior of these Cu alloys under high pH conditions.
In the present paper, the corrosion behavior of Cu alloys in NH3 and ETA solutions was investigated under conditions simulating the condensate water, feed water, and main steam systems. The effects of corrosion on the integrity of the alloys were determined by a tensile test.
The corrosion of the copper alloys was accompanied with the formation of oxide in the solution containing dissolved oxygen at 70°C. On the other hand, the selective dissolution of additional elements was observed in the solution without dissolved oxygen at 220 and 280°C. There was no apparent difference in the corrosion behavior of Cu alloys in NH3 solution and ETA solution. The corrosion rate of the Cu alloys increased with the Pb content in the alloys. Effects of the corrosion during the immersion test on tensile properties of Cu alloys were not observed.
論文アクセスランキング
26 Apr. (Last 30 Days)
-
Wettability of CaS Against Molten Iron at 1873 K
ISIJ International Vol.65(2025), No.2
-
Perspectives on the Promising Pathways to Zero Carbon Emissions in the Steel Industry toward 2050
ISIJ International Vol.65(2025), No.2
-
Thermodynamic evaluation of interaction parameters of solutes in molten iron
ISIJ International 早期公開
-
-
Prediction Studies of Strip Centering with Flotation Dryer
ISIJ International 早期公開
-
Ammonia as a Green Energy Carrier to Lower Blast Furnace CO2 Emissions
ISIJ International 早期公開
-
高感度電磁超音波による縦波横波ハイブリッド式連続鋳造クレーターエンド検知
鉄と鋼 Vol.111(2025), No.5
-
-
-
Preface
ISIJ International Vol.36(1996), No.Suppl
この機能はログイン後に利用できます。
下のボタンをクリックしてください。