材料と環境 Vol. 72 (2023), No. 9
Backnumber
-
Vol. 74 (2025)
-
Vol. 73 (2024)
-
Vol. 72 (2023)
-
Vol. 71 (2022)
-
Vol. 70 (2021)
-
Vol. 69 (2020)
-
Vol. 68 (2019)
-
Vol. 67 (2018)
-
Vol. 66 (2017)
-
Vol. 65 (2016)
-
Vol. 64 (2015)
-
Vol. 63 (2014)
-
Vol. 62 (2013)
-
Vol. 61 (2012)
-
Vol. 60 (2011)
-
Vol. 59 (2010)
-
Vol. 58 (2009)
-
Vol. 57 (2008)
-
Vol. 56 (2007)
-
Vol. 55 (2006)
-
Vol. 54 (2005)
-
Vol. 53 (2004)
-
Vol. 52 (2003)
-
Vol. 51 (2002)
-
Vol. 50 (2001)
-
Vol. 49 (2000)
-
Vol. 48 (1999)
-
Vol. 47 (1998)
-
Vol. 46 (1997)
-
Vol. 45 (1996)
-
Vol. 44 (1995)
-
Vol. 43 (1994)
-
Vol. 42 (1993)
-
Vol. 41 (1992)
-
Vol. 40 (1991)
キーワードランキング
02 Jul. (Last 30 Days)
材料と環境 Vol. 72 (2023), No. 9
銀の腐食故障モードと関連メカニズム
石川 雄一
pp. 234-242
DOI:
10.3323/jcorr.72.234抄録
As the second part of a series of articles describing corrosion behavior of silver, this article presents corrosion mechanism and failure modes seen for the electronic equipment under corrosive conditions. Inherent electrical bias associated with electronics application may cause electrolytic corrosion and electrochemical migration when the surface insulation resistance of dielectrics is reduced because of moisture absorption and condensation. Even a very thin tarnishing film formed may cause degradation of electrical and electronic performance as well as optical performance. Galvanic corrosion, corrosion product creep and whisker formation are also described.
他の人はこちらも検索
材料と環境 Vol.72(2023), No.9
環境試験による塗膜のアドミタンスと内部構造の変化
堀江 俊男, 北原 学, 谷 宗親, 浅井 幹雄
pp. 243-248
DOI:
10.3323/jcorr.72.243抄録
The impedance of the paint film varied depending on the environmental test. It is considered that the impedance spectrum of the coating films changed by the effects of water content in the paint film, polymer structure, and elements that penetrated the paint film. However, no clear relationship could be found between the impedance spectrum of the coating film and its internal structure. To understand the change in the impedance spectrum, we performed D-SIMS and AFM-IR analysis on the paint films after the environmental test. The results suggest that the admittance spectra may reflect the state of infracted moisture and elements into the coating films.
他の人はこちらも検索
材料と環境 Vol.72(2023), No.9
論文アクセスランキング
02 Jul. (Last 30 Days)
-
Perspectives on the Promising Pathways to Zero Carbon Emissions in the Steel Industry toward 2050
ISIJ International Vol.65(2025), No.2
-
Wettability of CaS Against Molten Iron at 1873 K
ISIJ International Vol.65(2025), No.2
-
-
Effect of Water on the Non-Isothermal Hydrogen-Water Reduction of Industrial Hematite Pellets
ISIJ International 早期公開
-
Effects of alloying-element addition on hydrogen diffusion and hydrogen absorption in Ni
ISIJ International 早期公開
-
Micromechanical characterization of nano-bainite steel
ISIJ International 早期公開
-
Investigation of the Effects of Mechanical Properties and Carbon Content on Cold Cracking in Laser Welds of High-strength Thin Steel Sheets
ISIJ International Vol.64(2024), No.10
-
Reaction-diffusion Kinetics Modelling of Coke Gasification in Simulated H2 Reduction Blast Furnace
ISIJ International Vol.65(2025), No.6
-
Stress-strain Curves from Self-fluxing Pellets Reduced with CO or H2
ISIJ International Vol.65(2025), No.6
-
Thermodynamic Evaluation of Interaction Parameters of Solutes in Molten Iron
ISIJ International Vol.65(2025), No.7
この機能はログイン後に利用できます。
下のボタンをクリックしてください。