材料と環境 Vol. 72 (2023), No. 11
Backnumber
-
Vol. 73 (2024)
-
Vol. 72 (2023)
-
Vol. 71 (2022)
-
Vol. 70 (2021)
-
Vol. 69 (2020)
-
Vol. 68 (2019)
-
Vol. 67 (2018)
-
Vol. 66 (2017)
-
Vol. 65 (2016)
-
Vol. 64 (2015)
-
Vol. 63 (2014)
-
Vol. 62 (2013)
-
Vol. 61 (2012)
-
Vol. 60 (2011)
-
Vol. 59 (2010)
-
Vol. 58 (2009)
-
Vol. 57 (2008)
-
Vol. 56 (2007)
-
Vol. 55 (2006)
-
Vol. 54 (2005)
-
Vol. 53 (2004)
-
Vol. 52 (2003)
-
Vol. 51 (2002)
-
Vol. 50 (2001)
-
Vol. 49 (2000)
-
Vol. 48 (1999)
-
Vol. 47 (1998)
-
Vol. 46 (1997)
-
Vol. 45 (1996)
-
Vol. 44 (1995)
-
Vol. 43 (1994)
-
Vol. 42 (1993)
-
Vol. 41 (1992)
-
Vol. 40 (1991)
キーワードランキング
17 May. (Last 30 Days)
材料と環境 Vol. 72 (2023), No. 11
防錆油について
長瀬 直樹
pp. 278-283
DOI:
10.3323/jcorr.72.278抄録
Rust preventive oil is used for relatively short periods of time, such as during storage and transportation during the manufacture of metal parts. It is one of the rust prevention means used for the purpose of temporary rust prevention for a period of time.
HCl水溶液中の溶存90Sr及び137CsがSUS 316Lの腐食電位に及ぼす影響
青山 高士, 佐藤 智徳, 上野 文義, 加藤 千明, 佐野 成人, 山下 直輝, 五十嵐 誉廣
pp. 284-288
DOI:
10.3323/jcorr.72.284抄録
In order to analyze the effect of beta particles in solution on the corrosion of Type 316L stainless steel, the effect of dissolved 90Sr on the corrosion potential was investigated. 90Sr standard solution and 137Cs standard solution were dropped into HCl while the corrosion potential was measured in HCl. As a result, the potential increase in the solution with 90Sr standard solution was larger than that in the solution with 137Cs standard solution. The results were verified by calculations, which show that the difference in the rate of formation of H2O2 in solution due to water radiolysis causes a difference in the change in potential in both solutions.
文化財建造物保存修理等に供する現代製鉄法による新たな和釘の耐食性評価
松本 雅充, 迫田 章人, 末廣 正芳, 西 隆之, 渡邊 緩子, 本弓 省吾
pp. 289-298
DOI:
10.3323/jcorr.72.289抄録
The purpose is to inherit the technical properties of the past as much as possible to manufacture Japanese nails, Wakugi, used for preservation and repair of Japanese wooden buildings. Therefore, we investigated the technical properties of Wakugi from the Azuchi-Momoyama period to the Edo period, when Tatara ironmaking reaches maturity, from the viewpoints of chemical composition, surface film structure, and corrosion resistance. Prevention of iron stain on wood and long-term corrosion resistance were evaluated by electrochemical measurements and accelerated corrosion tests on Wakugi made by hot forging by handmade work by blacksmiths.
論文アクセスランキング
17 May. (Last 30 Days)
-
Effect of Wettability on Droplet Agglomeration in Two Immiscible Liquids
ISIJ International 早期公開
-
-
Molecular Dynamics of Solidification
ISIJ International Vol.64(2024), No.7
-
Development of Heat-of-fusion Measurement for Metals Using a Closed-type Aerodynamic Levitator
ISIJ International Vol.64(2024), No.7
-
Thermodynamic Analysis on Slag/Metal Reactions in Steelmaking Process Using Direct Reduced Iron and Steel Scraps
ISIJ International Vol.64(2024), No.6
-
Dissolution of Carbon-Containing Species in CaO–SiO2–Al2O3 Slag
ISIJ International Vol.64(2024), No.6
-
Effect of Iron Oxide Dissolution on Thermochemical Property of Solid Solution between Ca2SiO4 and Ca3P2O8 at 1573 K
ISIJ International Vol.64(2024), No.6
-
Recycling Process for Net-Zero CO2 Emissions in Steel Production
ISIJ International 早期公開
-
Magnetic Crystalline Alignment
ISIJ International Vol.47(2007), No.4
-
Copper Distribution in Fe–Cu and Fe–C–Cu Alloys under Imposition of an Intense Magnetic Field
ISIJ International Vol.48(2008), No.7
この機能はログイン後に利用できます。
下のボタンをクリックしてください。